Sr. No.
|
Property
|
Unit
|
Test Method
|
Typical Values
|
General |
1
|
Thickness
|
Micron
|
GPL Method
|
12
|
19
|
23
|
36
|
50
|
75
|
100
|
125
|
2
|
Yield
|
M2/Kg
|
GPL Method
|
59.5
|
37.5
|
31.0
|
19.8
|
14.3
|
9.5
|
7.14
|
5.71
|
3
|
Density
|
gm/cc
|
ASTM-D-1505
|
1.4
|
1.4
|
1.4
|
1.4
|
1.4
|
1.4
|
1.4
|
1.4
|
4
|
Water Absoption
( Max )
|
%
|
ASTM-D-570
|
0.8
|
0.8
|
0.8
|
0.8
|
0.8
|
0.8
|
0.8
|
0.8
|
Mechanical |
1
|
Tensile Strength at break
( MD / TD )
|
Kg/cm2
|
ASTM-D-882
|
1900
|
1900
|
2000 |
2000 |
2000 |
1800 |
1700
|
1700
|
2
|
Elongation
( MD / TD )
|
%
|
ASTM-D-882
|
90
|
100
|
100
|
100
|
130
|
140
|
150
|
150
|
3
|
Slip(COF)
|
--
|
ASTM-D-1894
|
0.5
|
0.5
|
0.5
|
0.4
|
0.4
|
0.3
|
0.3
|
0.3
|
Optical |
1
|
Haze
|
%
|
ASTM-D-1003
|
3.5
|
4.0
|
5 .0
|
8 .0
|
10.0
|
10.0
|
10.0
|
30.0
|
Thermal |
1
|
Shrinkage @ 150 ー C 30 min
|
|
ASTM-D-1204
|
|
|
|
|
|
|
|
|
|
MD
|
% |
|
2.0
|
2.0 |
1.6
|
1.6
|
1.2
|
1.0
|
1.0
|
1.0
|
|
TD
|
% |
|
1.0
|
1.0
|
0.4
|
0.4
|
0.4
|
0.4
|
0.4
|
0.4
|
2
|
Melting Point
|
ーC
|
DSC
|
255
|
255
|
255
|
255
|
255
|
255
|
255
|
255
|
Electrical |
1
|
Break Down Voltage
(2" Electrode)
|
KV
|
ASTM-D-149
|
3.5
|
4.0
|
5.5
|
7.0
|
9.5
|
12.5
|
13.5
|
15.5
|
2
|
Surface Resistivity
|
Ohm
|
ASTM-D-257
|
1012 |
1012
|
1012
|
1012
|
1012
|
1012
|
1012
|
1012
|
3
|
Volume Resistivity @ RT
|
Ohm cm
|
ASTM-D-257
|
1016 |
1016 |
1016 |
1016 |
1016 |
1016 |
1016 |
1016 |
4
|
Permitivity
23ーC,50Hz
23ーC,1kHz
23ーC,10 kHz
0ーC,50Hz
50ーC,50Hz
100ーC,50Hz
150ーC,50Hz
|
---
|
IEC 250
|
3.26
3.24
3.21
3.26
3.27
3.35
3.65
|
5 |
Dissipation Factor
23ーC,50Hz
23ーC,1kHz
23ーC,10 kHz
0ーC,50Hz
50ーC,50Hz
100ーC,50Hz 150ーC,50Hz
|
---
|
IEC 250
|
0.002
0.0055
0.011
0.004
0.0015
0.007
0.006
|
6
|
Coeff of Thermal Expansion between 20ーC &
50ー C
|
1/ K(cm/cm ーC)
1/ K(cm/cm ーC)
|
--
--
|
34X10-6 ( MD )
28X10-6 ( TD )
|
Chemical Resistance |
|
Dilute Acids & Alkalis
Concentrated Alkalis
Concentrated Hydrochloric Acid
Concentrated Sulphuric Acid
Greases,Oils & Fats
Organic Solvents , Alcohols & Hydrocarbons
|
Good
Poor
Fair
Poor
Good
Good |
|
Ketones, Esters & Chlorinated Compounds |
Fairly Good |
|
Phenols,Cresols & Chlorinated Phenols
|
Poor
|
Roll |
1
|
Width -Max
|
mm
|
GPL METHOD
|
2400 |
2100 |
2100 |
1630 |
1630 |
1850 |
1850 |
1850 |
2
|
Standard length -Min |
Mtrs
|
GPL METHOD |
6000 |
3300 |
1650 |
1050 |
750 |
500 |
375 |
300 |
3
|
Standard length -Max |
Mtrs
|
GPL METHOD |
36000 |
8000 |
18500 |
8400 |
6750 |
4500 |
3375 |
2700 |
Pancake |
1
|
Width -Min
|
mm
|
GPL METHOD |
NA |
NA |
11 |
11 |
11 |
11 |
11 |
11 |
2
|
Width -Max |
mm
|
GPL METHOD |
NA |
NA |
150 |
150 |
150 |
150 |
150 |
150 |
3
|
Standard length -Min |
Mtrs
|
GPL METHOD |
NA |
NA |
1650 |
1050 |
750 |
500 |
375 |
300 |
4
|
Standard length -Max |
Mtrs
|
GPL METHOD |
NA |
NA |
6600 |
4200 |
3000 |
2000 |
1500 |
1200 |